[ Source：　|　Author：This station　|　Publication Time：2018-02-28 |　Browse：468Number ]

At the beginning of 2018, AQSIQ took spot checks on processed aluminum and titanium alloy products At the beginning of 2018, AQSIQ examined a total of aluminum and titanium alloy processed products in Beijing, Tianjin, Hebei, Shanxi, Inner Mongolia, Heilongjiang, Jilin, Liaoning, Shanghai, Jiangsu 384 enterprises in 28 provinces, autonomous regions and municipalities including Zhejiang, Anhui, Fujian, Jiangxi, Shandong, Henan, Hubei, Hunan, Guangdong, Guangxi, Sichuan, Guizhou, Yunnan, Shaanxi, Gansu, Qinghai, Ningxia, batch.

The spot checks according to GB / T 5237.1-2008 "aluminum alloy building profiles Part 1 substrate", GB / T 5237.2-2008 "aluminum alloy building profiles Part 2 anodized profiles", GB / T 5237.3-2008 "aluminum alloy Building profiles - Part 3 Electrophoretic paint profiles ", GB / T 5237.4-2008" Aluminum alloy profiles - Part 4 Powder-coated profiles ", GB / T 5237.5-2008" Aluminum alloy profiles - Part 5 Fluorocarbon paint profiles " , GB / T 5237.6-2012 "aluminum alloy building profiles Part 6 insulation profiles" and other standards, the chemical composition of aluminum profiles (silicon, iron, copper, manganese, magnesium, chromium, zinc and titanium) , Tensile strength, non-proportional extension strength, elongation at break, minimum nominal wall thickness, wall thickness deviation, average film thickness, oxide film local film thickness, oxide film average film thickness, oxide film sealing quality, Film thickness, partial thickness of the composite film, hardness of the film, dry adhesion of the paint film, wet adhesion of the paint film, alkali resistance, minimum local thickness of the coating, dry adhesion of the coating, wet adhesion of the coating, Adhesion, coating indentation hardness, coating level According to GB / T 26060-2010 "Titanium and titanium alloy ingot", GB / T 3621 (GB / T3621), the thickness of the coating, the minimum local film thickness of the coating, the hardness of the coating and the longitudinal shear characteristics (room temperature) -2007 "Titanium and titanium alloy sheet", GB / T 3622-2012 "Titanium and titanium alloy with foil," GB / T 3624-2010 "titanium and titanium alloy seamless pipe", GB / T 26058-2010 Titanium and Titanium Alloy Extruded Tubes, GB / T 26057-2010 Titanium and Titanium Alloy Welded Tubes, GB / T 3625-2007 Titanium Tubes and Titanium Alloy Tubes for Heat Exchanger and Condenser, GB / T 2965 -2007 "Titanium rods and titanium alloy rods", GB / T 3623-2007 "Titanium wire and titanium alloy wire" and other standards, the chemical composition of titanium and titanium alloy products (iron, carbon, hydrogen, oxygen, N, Al, Sn, Mo, V, Zr, Si, Nb, B, Mn, Pd, Ni, Cr, Cu and Mg) Tensile strength Flat experiments, flared experiments, low magnification and other 26 projects were tested.

Spot checks found that 74 batches of products do not meet the standards, related to iron, copper, zinc, manganese, tensile strength, the provisions of non-proportional extension strength, minimum nominal wall thickness, wall thickness deviation, the average film thickness, Local film thickness of anodic oxide film, local film thickness of the film, hardness of the film, partial film thickness of the composite film, alkali resistance, sealing quality, longitudinal shear characteristic value (room temperature), elongation at break, flattening experiment Mouth experiment, low magnification project.

At the beginning of 2018, AQSIQ took spot checks on processed aluminum and titanium alloy products At the beginning of 2018, AQSIQ examined a total of aluminum and titanium alloy processed products in Beijing, Tianjin, Hebei, Shanxi, Inner Mongolia, Heilongjiang, Jilin, Liaoning, Shanghai, Jiangsu 384 enterprises in 28 provinces, autonomous regions and municipalities including Zhejiang, Anhui, Fujian, Jiangxi, Shandong, Henan, Hubei, Hunan, Guangdong, Guangxi, Sichuan, Guizhou, Yunnan, Shaanxi, Gansu, Qinghai, Ningxia, batch.

The spot checks according to GB / T 5237.1-2008 "aluminum alloy building profiles Part 1 substrate", GB / T 5237.2-2008 "aluminum alloy building profiles Part 2 anodized profiles", GB / T 5237.3-2008 "aluminum alloy Building profiles - Part 3 Electrophoretic paint profiles ", GB / T 5237.4-2008" Aluminum alloy profiles - Part 4 Powder-coated profiles ", GB / T 5237.5-2008" Aluminum alloy profiles - Part 5 Fluorocarbon paint profiles " , GB / T 5237.6-2012 "aluminum alloy building profiles Part 6 insulation profiles" and other standards, the chemical composition of aluminum profiles (silicon, iron, copper, manganese, magnesium, chromium, zinc and titanium) , Tensile strength, non-proportional extension strength, elongation at break, minimum nominal wall thickness, wall thickness deviation, average film thickness, oxide film local film thickness, oxide film average film thickness, oxide film sealing quality, Film thickness, partial thickness of the composite film, hardness of the film, dry adhesion of the paint film, wet adhesion of the paint film, alkali resistance, minimum local thickness of the coating, dry adhesion of the coating, wet adhesion of the coating, Adhesion, coating indentation hardness, coating level According to GB / T 26060-2010 "Titanium and titanium alloy ingot", GB / T 3621 (GB / T3621), the thickness of the coating, the minimum local film thickness of the coating, the hardness of the coating and the longitudinal shear characteristics (room temperature) -2007 "Titanium and titanium alloy sheet", GB / T 3622-2012 "Titanium and titanium alloy with foil," GB / T 3624-2010 "titanium and titanium alloy seamless pipe", GB / T 26058-2010 Titanium and Titanium Alloy Extruded Tubes, GB / T 26057-2010 Titanium and Titanium Alloy Welded Tubes, GB / T 3625-2007 Titanium Tubes and Titanium Alloy Tubes for Heat Exchanger and Condenser, GB / T 2965 -2007 "Titanium rods and titanium alloy rods", GB / T 3623-2007 "Titanium wire and titanium alloy wire" and other standards, the chemical composition of titanium and titanium alloy products (iron, carbon, hydrogen, oxygen, N, Al, Sn, Mo, V, Zr, Si, Nb, B, Mn, Pd, Ni, Cr, Cu and Mg) Tensile strength Flat experiments, flared experiments, low magnification and other 26 projects were tested.

Spot checks found that 74 batches of products do not meet the standards, related to iron, copper, zinc, manganese, tensile strength, the provisions of non-proportional extension strength, minimum nominal wall thickness, wall thickness deviation, the average film thickness, Local film thickness of anodic oxide film, local film thickness of the film, hardness of the film, partial film thickness of the composite film, alkali resistance, sealing quality, longitudinal shear characteristic value (room temperature), elongation at break, flattening experiment Mouth experiment, low magnification project.